Depositing diamond film on high Co content cemented carbide using CrSiN film as an interlayer

doi: 10.13394/j.cnki.jgszz.2023.0004
More Information
  • Received Date: 2023-01-04
  • Accepted Date: 2023-04-27
  • Rev Recd Date: 2023-04-18
  • Available Online: 2023-05-07
  • In order to solve the problem that it is difficult to grow diamond films with high binding force on the surface of high cobalt cemented carbide, the Cr/CrSiN film was used as the transition layer, and the nanocrystalline diamond films (NCD), the submicrocrystalline diamond films (SMCD) and the microcrystalline diamond films (MCD) were deposited on the cemented carbide by hot filament chemical vapor deposition method, and their binding forces were studied. The results show that the Cr/CrSiN transition layer can be used to deposit diamond films with excellent bonding strength on the surface of high cobalt cemented carbide. NCD has the best binding force, followed by SMCD, and MCD has the worst binding force. When the grain size of the diamond film increases, the bonding forces of the diamond film weaken due to the poor toughness of the diamond films and severe carbonization of the transition layer. When the crystal size of the diamond film increases, the binding force of the diamond film becomes weak due to the poor toughness of the diamond film and serious carbonization of the transition layer.

     

  • loading
  • [1]
    梅沢三造. 硬质合金刀具常识及使用方法 [M]. 北京: 机械工业出版社, 2009.

    UMEZAWA Sanzo. General knowledge and instruction of cemented carbide cutting tools [M]. Beijing: China Machine Press, 2009.
    [2]
    孙宝琦, 何平. 模具用硬质合金及其进展 [J]. 模具工业,1996(12):3-7. doi: 10.16787/j.cnki.1001-2168.dmi.1996.12.001

    SUN Baoqi, HE Ping. Cemented carbide for a mould and its development [J]. Die & Mould Industry,1996(12):3-7. doi: 10.16787/j.cnki.1001-2168.dmi.1996.12.001
    [3]
    孔维星, 巩春志, 田修波. 微细硬质合金刀具沉积金刚石薄膜的形核研究 [J]. 真空与低温,2019,25(3):170-177. doi: 10.3969/j.issn.1006-7086.2019.03.004

    KONG Weixing, GONG Chunzhi, TIAN Xiubo. Nucleation research of diamond films on tiny hard alloy milling cutters [J]. Vacuum & Cryogenics,2019,25(3):170-177. doi: 10.3969/j.issn.1006-7086.2019.03.004
    [4]
    王云, 谢小豪, 汪艳亮, 等. 硬质合金刀具涂层的研究进展 [J]. 有色金属科学与工程,2019,10(1):60-66. doi: 10.13264/j.cnki.ysjskx.2019.01.010

    WANG Yun, XIE Xiaohao, WANG Yanliang, et al. Latest progress in the preparation of cemented carbide tool coatings [J]. Nonferrous Metals Science and Engineering,2019,10(1):60-66. doi: 10.13264/j.cnki.ysjskx.2019.01.010
    [5]
    CHANDRAN M, HOFFMAN A. Diamond film deposition on WC-Co and steel substrates with a CrN interlayer for tribological applications [J]. Journal of Physics D: Applied Physics,2016,49(21):213002.
    [6]
    PENG J H, ZENG J W, XIAO Y, et al. Novel conversion annealing pretreatment for improved deposition of diamond coatings onto WC-Co cemented carbide [J]. Journal of Alloys and Compounds,2022,893:1-12.
    [7]
    ZHENG K, GAO J, HEI H J, et al. Design and fabrication of HfC, SiC/HfC and HfC-SiC/HfC interlayers for improving the adhesion between diamond coatings and cemented carbides [J]. Journal of Alloys and Compounds,2020,815:1-8.
    [8]
    XU F, XU J H, YUEN M F, et al. Adhesion improvement of diamond coatings on cemented carbide with high cobalt content using PVD interlayer [J]. Diamond and Related Materials,2013,34:70-75. doi: 10.1016/j.diamond.2013.01.012
    [9]
    POLINI R, BARLETTA M. On the use of CrN/Cr and CrN interlayers in hot filament chemical vapour deposition (HF-CVD) of diamond films onto WC-Co substrates [J]. Diamond and Related Materials,2008,17(3):325-335. doi: 10.1016/j.diamond.2007.12.059
    [10]
    HEI H, SHEN Y, MA J, et al. Effect of substrate temperature on SiC interlayers for diamond coatings deposition on WC-Co substrates [J]. Vacuum,2014,109:15-20. doi: 10.1016/j.vacuum.2014.06.001
    [11]
    PARK J K, LEE H J, LEE W S, et al. Effect of TiAl-based interlayer on the surface morphology and adhesion of nanocrystalline diamond film deposited on WC-Co substrate by hot filament CVD [J]. Surface and Coatings Technology,2014,258:108-113. doi: 10.1016/j.surfcoat.2014.09.053
    [12]
    FISCHER M, CHANDRAN M, AKHVLEDIANI R, et al. Interplay between adhesion and interfacial properties of diamond films deposited on WC-10%Co substrates using a CrN interlayer [J]. Diamond and Related Materials,2016,70:167-172. doi: 10.1016/j.diamond.2016.10.021
    [13]
    LI X, WANG C C, CHEN C K, et al. Thickness-controllable diamond films deposited on stainless steel using a Cr/Cr-Si-N interlayer prepared at different N2/Ar flow ratios [J]. Applied Surface Science,2020,532:1-10.
    [14]
    LYU F, LI X, CHEN C K, et al. High adhesion diamond films deposited on stainless steel by using nanocomposite films with mosaic interface as an interlayer [J]. Applied Surface Science,2020,528:1-10.
    [15]
    李晓, 刘成, 陈道勇, 等. 过渡层Cr/Cr-Si中Si含量对不锈钢表面生长金刚石薄膜的影响 [J]. 硅酸盐学报,2020,48(4):608-614. doi: 10.14062/j.issn.0454-5648.20190631

    LI Xiao, LIU Cheng, CHEN Daoyong, et al. Effect of Si content on Cr/Cr-Si interlayer on diamond film growth on stainless steel surface [J]. Journal of the Chinese ceramic society,2020,48(4):608-614. doi: 10.14062/j.issn.0454-5648.20190631
    [16]
    RALCHENKO V G, SMOLIN A A, PEREVERZEV V G, et al. Diamond deposition on steel with CVD tungsten intermediate layer [J]. Diamond and Related Materials,1995,4(5/6):754-758.
    [17]
    CHANDRAN M, SAMMLER F, UHLMANN E, et al. Wear performance of diamond coated WC-Co tools with a CrN interlayer [J]. Diamond and Related Materials,2017,73:47-55. doi: 10.1016/j.diamond.2016.12.001
    [18]
    PICKRELL D J, KLINE K A, TAYLOR R E. Thermal-expansion of polycrystalline diamond produced by chemical-vapor-deposition [J]. Applied Physics Letters,1994,64(18):2353-2355. doi: 10.1063/1.111612
    [19]
    PIERSON H O. Handbook of refractory carbides and nitrides [M]. Holland: Elsevier Science, 1996.
    [20]
    GAO J, HEI H J, ZHENG K, et al. Design and synthesis of diffusion-modified HfC/HfC-SiC bilayer system onto WC-Co substrate for adherent diamond deposition [J]. Journal of Alloys and Compounds,2017,705:376-383. doi: 10.1016/j.jallcom.2016.10.316
    [21]
    SAILS S R, GARDINER D J, BOWDEN M, et al. Monitoring the quality of diamond films using Raman spectra excited at 514.5 nm and 633 nm [J]. Diamond and Related Materials,1996,5(6/7/8):589-591.
    [22]
    VIDAKIS N, ANTONIADIS A, BILALIS N. The VDI 3198 indentation test evaluation of a reliable qualitative control for layered compounds [J]. Journal of Materials Processing Technology,2003,143/144:481-485.
    [23]
    郭涛. 脆性薄膜的失效及其对基体的影响 [D]. 北京: 北京科技大学, 2018.

    GUO Tao. The failure of brittle film and its influence on the underlying substrate [D]. Beijing: University of Science and Technology Beijing, 2018.
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Figures(6)  / Tables(1)

    Article Metrics

    Article views (379) PDF downloads(31) Cited by()
    Proportional views
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return